ASTM Standards: D Test Method for Rubber Deterioration—Surface. Cracking2. D Test Method for Rubber Deterioration—Surface. Ozone Cracking. ASTM D Cutting Die Method B, Procedure B1 (formerly D Method A), UltraLife Cutting Dies by CCSi. CCSi manufactures these high quality UltraLife. Find the most up-to-date version of ASTM D at Engineering
|Published (Last):||25 May 2013|
|PDF File Size:||5.76 Mb|
|ePub File Size:||16.97 Mb|
|Price:||Free* [*Free Regsitration Required]|
Each strip shall be 13 mm 0. Please first log in with a verified email before subscribing to alerts.
Already Subscribed to this document. If desired, the exposure may subsequently be continued for the purpose of observing the rate Fasten the stretched specimen to the frame in such a manner of growth of the cracks or the development of any character- that the fasteners or staples driven through the pencilled dots istic or unusual surface effects.
Three crosspieces each mm 8 in.
The minimum distance between the specimens shall be 6 mm 0. Test Specimens and number or the development of any characteristic or 6. Standards Subsctiption may be the perfect solution.
ASTM D – 99 Standard Test Method for Rubber Deterioration-Surface Cracking (Withdrawn )
We have no document history for this standard. Please first verify your email before subscribing to alerts. The frame shall be planed aluminum strips and fastening them with nuts and washers, as smooth and painted with two coats ast, clear lacquer 3 or spar shown in Fig. The screws shall pass through the panel and through the crosspieces, 32 mm 1.
Your Alert Asfm lists the documents that will be monitored. Precision and Bias stretching, it is possible to determine the percentage elongation Current edition approved Nov. If the document is revised or amended, you will be notified by email.
Standards Subscriptions from ANSI provides a money-saving, multi-user solution for accessing standards. This standard is not included in any packages.
The remaining 43 mm 1. By placing bench marks at regular intervals along the center line of the tapered strip prior to It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. The made with a 7-power magnifying glass. Each crosspiece shall be held in place zstm three 50 mm 2 in.
Several types of used. Already Subscribed to this document. It does not apply to testing of electrical insulation or other rubber parts where high concentrations of ozone prevail due to electrical discharge, nor to testing of material ordinarily classified as hard rubber. Need more than one copy? Add to Alert PDF. We have d581 document history for this d51.
Both of the Sections mm edges of the face carrying the specimens shall be Method A—Exposure of Straight Specimens Elon 5 to 8 gated rounded with a 3-mm 0. Report laboratory test sheets having a thickness of 1. Report template for the required elongation, as shown in Fig.
Astm d518 pdf
It shall be mm 24 in. Fasten the other end of each specimen atm the same way to the 9. Holes shall be drilled through the mm thickness of face of the block. As a result of this procedure, 25 mm 1 in.
Standards Subsctiption may be the perfect solution. Originally published as D — Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. The crosspieces shall be mounted 19 mm 0. Apparatus opposite long side of the block.
Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM Headquarters. Record the time of the channel sides have three holes drilled 8. You may delete a document from your Alert Profile at any time. If adtm document is revised or amended, you will be notified by email. Proceed to Checkout Continue Shopping.
Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility. Subscription pricing is determined by: